Experiments were carried out the phenomenal observation on effect of corona treated hotmelt laminating film in process of manufacture by 2 kinds of rolling speed and electric power variatons. Surface treatment by corona which is exposure of film surface to electron of ion bombardment, rather than mere exposure to active species, like atomic oxygen or ozone, can enhance adhesion by removing contaminant, electret, roughening surface, and introducing reactive chemical group. Reactive neutrals, ions, electron and photons generated during the corona treatment interact simultaneously with polymers to alter surface chemical composition, wettability, and thus film adhesion. However, it is highly recommended that extensive chains scission is avoided because it can lead to side-effect by forming sticky matter, resulting in dropouts. This paper reviews principles of surface preparation of polypropylene substrate by corona discharging. In addition, the experimental section provides a description of parameter optimization on corona discharging treatment and its side-effect. Experimental results are discussed in terms of surface wetting as determined by contact angle and SEM measurements. When the rolling speed of the film decreased from 1.666 [m / sec] to 0.083 [m / sec], contact angle decreased from 80 [°] to 64 [°], and the wettability was greatly improved. As the supply power increased from 0.4 [kVA] to 2 [kVA] at the corona discharge surface treatment, the contact angle decreased from 77 [°] to 65 [°], and the wettability was greatly improved.